Influence of NaHCO3 powder on color and roughness of the composite submitted to bleaching and euterpe oleracea / Influencia del polvo de NaHCO 3 en el color y rugosidad del composite sometido a blanqueo y euterpe oleracea

Aim: This study aims to evaluate the surface roughness and susceptibility to staining of bleached composite resin with 22% carbamide peroxide, as well as the effect of subsequent prophylaxis with NaHCO3 powder. Material and Methods: Forty disk-shaped (2 × 6 mm) specimens of composite resin (Z250 XT) were prepared. Half of the specimens were subjected to bleaching with 22% carbamide peroxide, and the other half were stored in artificial saliva. In sequence, all specimens were immersed in acai juice (Euterpe oleracea) for 4 h for 14 days, and subdivided into two groups. Group 1 samples were subjected to prophylaxis treatment, while group 2 samples were subjected to treatment with artificial saliva. Surface roughness (Ra) and color (ΔE*) were measured after polishing (T0), bleaching (T1), immersion in acai juice (T2), and application of NaHCO3 powder (T3) using a profilometer and a spectrophotometer. Results: Statistical analyses (analysis of variance and Tukey's test, p≤0.05) revealed that regarding color there was statistically significance for the factors in isolation, except for the factor bleaching. For both color and surface roughness there was statistically significant difference for the interaction, except for the interaction between NaHCO3 power and bleaching. Conclusion: The NaHCO3 air-powder polishing decreases the staining of the composite resin; however, it increases the surface roughness. With respect to the color variable, the whitening factor had no significant effect on the tested material; however, it increases surface roughness.

Objetivo: Este estudio tiene como objetivo evaluar la rugosidad de la superficie y la susceptibilidad a la tinción de la resina compuesta blanqueada con peróxido de carbamida al 22%, así como el efecto de la profilaxis posterior con polvo de NaHCO3. Material y Métodos: Se prepararon cuarenta especímenes en forma de disco (2 × 6 mm) de resina compuesta (Z250 XT). La mitad de los especímenes se sometieron a blanqueo con peróxido de carbamida al 22% y la otra mitad se almacenó en saliva artificial. En secuencia, todos los especímenes se sumergieron en jugo de acai (Euterpe oleracea) durante 4h durante 14 días, y se subdividieron en dos grupos. Las muestras del grupo 1 se sometieron a tratamiento profiláctico, mientras que las muestras del grupo 2 se sometieron a tratamiento con saliva artificial. La rugosidad de la superficie (Ra) y el color (ΔE*) se midieron después del pulido (T0), el blanqueo (T1), la inmersión en jugo de acai (T2) y la aplicación de polvo de NaHCO3 (T3) utilizando un perfilómetro y un espectrofotómetro. Resultados: Los análisis estadísticos (análisis de varianza y prueba de Tukey, p≤0.05) revelaron que en relación al color hubo significancia estadística para los factores en forma aislada, excepto para el factor blanqueamiento. Tanto para el color como para la rugosidad de la superficie hubo una diferencia estadísticamente significativa para la interacción, excepto para la interacción entre el poder de NaHCO3 y el blanqueo. Conclusión: El pulido al aire con polvo de NaHCO3 disminuye el manchado de la resina compuesta; sin embargo, aumenta la rugosidad de la superficie. Con respecto a la variable color, el factor de blanqueamiento no tuvo efecto significativo sobre el material ensayado; sin embargo, aumenta la rugosidad de la superficie.

Metal-ceramic partial fixed dentures: a retrospective study / Estudo retrospectivo de próteses parciais fixas metalocerâmicas

ABSTRACT Objective Metal-ceramic prosthesis are the treatment of choice in oral rehabilitation because of their high survival rates. However, there are few reports in the scientific literature about factors that lead to fractures of metal-ceramic prostheses. The aim of this study was to evaluate whether prostheses units number, abutment type and number, type of the prostheses, prostheses position in the mouth, bruxism and occlusal plaque influence the incidence of fractures in fixed metal-ceramic prostheses. Methods For this study, 16 patients were selected, totaling 74 metal-ceramic prostheses installed between 2000-2010, with follow up of at least four years. Besides dental history, other information was collected, such as patients' gender and age, prostheses installation date, and the ceramic system used. In case of prostheses fracture, a questionnaire was applied to identify signs of bruxism. A clinical evaluation was done to evaluate the prostheses integrity and opposing dentition characteristics. Success, failure and survival rates were determined. Results The results showed that the success rate of metal-ceramic prostheses was 87.8% and the survival rate was 89.1%. In addition, the success rate was independent of patient age, prostheses installation time, number of prosthesis, number of prosthesis' units and abutments. The qualitative variables also did not show significant statistical results between success and failure rates. Conclusion It was concluded that metal-ceramic prostheses have high success and survival rates, what guarantees longevity and indication of this type of prostheses in daily practice.

RESUMO Objetivo As próteses metalocerâmicas apresentam altas taxas de sobrevivência e, por isso, são indicadas para diversos casos em reabilitação oral. Entretanto, na literatura científica, existem poucos relatos clínicos sobre os fatores que levam à fratura dessas restaurações. Diante do exposto, o presente estudo teve como objetivo avaliar se a quantidade de elementos que compõem a prótese, se a quantidade de elementos por retentor, se o tipo de prótese e tipo de pilar, bem como sua localização, e o bruxismo, influenciam ou não nas fraturas dessas restaurações indiretas. Métodos Para isso, selecionaram-se 74 próteses metalocerâmicas, instaladas entre 2000 e 2010 em 16 pacientes, com acompanhamento mínimo de quatro anos. Foram coletadas informações dos pacientes, como: gênero, idade, data da instalação das próteses e cerâmica utilizada. Durante a avaliação clínica, observou-se a integridade da prótese e, em caso de fratura, coletava-se informações sobre a história clínica. As características do dente antagonista também foram avaliadas. Além disso, aplicou-se um questionário, com o intuito de identificar a provável presença de bruxismo. Resultados Como resultado, tem-se que a taxa de sucesso das próteses metalocerâmicas foi de 87,8% e, a taxa de sobrevivência, foi de 89,1%. A taxa de sucesso não teve influência da idade, tempo de instalação, número de próteses na boca, número de elementos ou pilares. Conclusão Embora pouco frequente, a fratura da cerâmica de cobertura foi a complicação mais comum. As próteses metalocerâmicas possuem altas taxas de sobrevida e de sucesso, o que garante a longevidade e a indicação desse tipo de restauração.

Color evaluation of a resin cement light polymerized by different light sources and submitted to potentially staining beverages / Avaliação da cor de um cimento resinoso fotopolimerizado por diferentes fontes de luz e submetidos a bebidas potencialmente corantes

Introduction: The color stability of resin cements, whether dual-pre-cured or photopolymerizable, as well as the color of the dental substrate, are fundamental for the aesthetic success of ceramic restorations, since the ceramic presents a high level of translucency due to its small thickness. Objective: The aim of this in vitro study was to evaluate the color of a resin cement light polymerized by different light sources and immersed in potentially staining beverages. Material and method: Were made 42 specimens of resin cement Variolink-Esthetic (2×6mm) (n=7), being half polymerized with LED light (F1) and half with Halogen light (F2). The specimens were stored in artificial saliva at 37 °C±1 °C. After 24 hours, they were polished with abrasive discs, and divided for the purpose of being submitted to the different solutions for 2 minutes per day, for 28 days, as follows: S1 - Coca-Cola; S2 - Red Wine; and S3 - Distilled Water (Control). Five color readouts were taken: T0 - initial; T1 - 7 days; T2 - 14 days; T3 - 21 days; and T4 - 28 days; with a spectrophotometer (Model SP62S). The color change data (ΔE*) were submitted to statistical analysis, ANOVA and Tukey (p≤0.05). Result: Analyzing the factor solution, S2 (5.89 (±0.02)), produced a higher ΔE* value than S1 (3.79 (±0.02)) and (S1), a higher value than S3 (1.41 (±0.02)). Analyzing the factor light source, F2 (4.05 (±0.12)), produced a higher ΔE* value than F1 (3.33 (±0.12)). When analyzing the factor time, ΔE* values were found to increase gradually over the course of time: T1(2.36 (±0.08)); T2(3.27 (±0.08)); T3(4.06 (±0.08)); and T4(5.09 (±0.08)). Conclusion: It was concluded that red wine produced a greater color change; Halogen light promoted highest degree of pigmentation; and the longer the time of immersion, the greater the color change of the material.

Introdução: A estabilidade de cor dos cimentos resinosos, sejam eles de presa dual ou fotopolimerizáveis, assim como a cor do substrato dental, são fundamentais para o sucesso estético das restaurações cerâmicas uma vez que a cerâmica apresenta alto nível de translucidez devido a sua pequena espessura. Objetivo: O objetivo deste estudo in vitro foi avaliar a cor de um cimento resinoso fotopolimerizado por diferentes fontes de luz e imersos em bebidas potencialmente corantes. Material e método: Foram confeccionados 42 espécimes do cimento resinoso Variolink-Esthetic (2×6mm) (n=7), sendo metade fotopolimerizado com luz LED (F1) e metade com luz Halógena (F2). Os espécimes foram mantidos em saliva artificial à 37 °C±1 °C. Após 24 horas, foram polidos com discos abrasivos e subdivididos para serem imersos 2 minutos por dia, durante 28 dias, nas diferentes soluções: S1 - Coca-Cola; S2 - Vinho Tinto; e S3 - Água destilada (controle). Foram realizadas 5 leituras de cor: T0 - inicial; T1 - 7 dias; T2 - 14 dias; T3 - 21 dias; e T4 - 28 dias; com auxílio de um espectrofotômetro (modelo SP62S). Os dados de alteração de cor (ΔE*) foram submetidos a análise estatística, ANOVA e Tukey (p≤0,05). Resultado: Analisando o fator solução, S2 (5,89 (±0,02)), proporcionou maior ΔE* que S1 (3,79 (±0,02)) e este (S1), maior que S3 (1,41 (±0,02)). Analisando o fator fonte de luz, F2 (4,05 (±0,12)), proporcionou maior ΔE* que F1 (3,33 (±0,12)). E analisando o fator tempo, obteve-se que ΔE* foi gradativamente aumentando no decorrer do tempo: T1(2,36 (±0,08)); T2(3,27 (±0,08)); T3(4,06 (±0,08)); e T4(5,09 (±0,08)). Conclusão: Conclui-se que o vinho tinto promoveu maior alteração de cor; a luz Halógena promoveu maior pigmentação e; quanto maior o tempo de imersão, maior alteração de cor do material.

Influência das desadaptações angulares unilaterais na distribuição de tensões da região peri-implantar de elementos unitários tipo UCLA submetidos a pré-carga e carga axial: estudo in vitro / Influence of the unilateral angular misfit in frameworks made of UCLA on the peri-implant strain distribution, subjected to preload and axial load

Atualmente, os implantes são utilizados em diversos tipos de tratamento na reabilitação oral. Para manutenção da osseointegração, é essencial que o conjunto prótese/implante/osso seja submetido a forças às quais estejam aptos a suportar. Os diferentes tipos de desadaptações das infraestruturas das próteses sobre implantes são fatores que podem contribuir para o aumento das tensões na região peri-implantar. Este estudo teve como objetivo avaliar a influência das desadaptações angulares unilaterais na distribuição de tensões na região periimplantar de pilares tipo UCLA, no momento da pré-carga e carga axial. Infraestruturas de CoCr, confeccionadas utilizando-se pilares tipo UCLA, foram divididas em quatro grupos: Grupo A (adaptado), Grupo B, Grupo C e Grupo D (50, 100 e 200 μm de desadaptação unilateral angular por vestibular, respectivamente). Cada grupo foi representado por quatro infraestruturas (n=4). Quatro implantes (4.1mm/15mm) foram posicionados em uma matriz metálica, onde posteriormente foi vazado o poliuretano (PU), com função de simular o tecido ósseo. Quatro extensômetros (strain gauges) foram posicionados na região vestibular, distal, lingual e mesial de cada implante, para aferir a quantidade de deformação; cada grupo foi posicionado em seu respectivo implante. Foram realizados dois testes: o teste de pré-carga com um torque de 32Ncm e o teste de carga com uma força axial estática de 300N. Cada infraestrutura foi sujeita aos dois testes, por cinco vezes. Para análise estatística dos dados, foram utilizados ANOVA (dois critérios) e o teste de Tukey (p<0,05). Os resultados mostraram que os grupos A e B tiveram menos deformação da região peri-implantar em ambos os testes, quando comparados aos grupos C e D. A estatística também mostrou que o Grupo A apresentou melhor distribuição de tensões em sua região, peri-implantar quando comparado aos outros três grupos (p<0,05). Como conclusões, este estudo mostrou que as desadaptações influem...

Nowadays implants are used in several kinds of oral rehabilitation treatments. For the osseointegration maintenance it is important that crow/implant/bone are subjected to forces which are able to withstand. Different kinds of misfit on the crown frameworks are factors that could lead to an increase of strain around the implanted bone. This study aimed to evaluate the influence of the unilateral angular misfit in frameworks made of UCLA on the peri-implant strain distribution, subjected to preload and axial load. Frameworks made of chrome-cobalt were fabricated on UCLA abutments and divided in 4 groups: Group A (no misfit), Group B, Group C, Group D (50, 100, and 200 of unilateral angular misfit by buccal side, respectively). Each group was represented for 4 frameworks (n=4). Four implants (4.1mm/15mm) were positioned in a metallic matrix which was subsequently poured the polyurethane (PU) to simulate the bone. Four strain gauges were positioned on the buccal, distal, lingual and mesial sides of each implant to assess the amount of strain, each group was connected on its respectively implant. It was performed 2 tests: the preload test with a 32Ncm torque and the load test by applying an axial force of 300N. Each framework was subjected to the both test five times. To the statistics analysis ANOVA (2 ways) and Turkeys test were performed. The results showed that the Groups A and B presented less deformation when compared to Groups C and D. The statistics also showed that the Group A presented better distribution of strain on its peri-implant bone when compared to the other three groups (p<0,05). In conclusion this study showed that misfit had influence on the strain distribution on the peri-implant bone and that strain increased on the Groups C and D which presented higher levels of misfit.

Influência das desadaptações angulares unilaterais na distribuição de tensões da região peri-implantar de elementos unitários tipo UCLA submetidos a pré-carga e carga axial: estudo in vitro / Influence of the unilateral angular misfit in frameworks made of UCLA on the peri-implant strain distribution, subjected to preload and axial load

Atualmente, os implantes são utilizados em diversos tipos de tratamento na reabilitação oral. Para manutenção da osseointegração, é essencial que o conjunto prótese/implante/osso seja submetido a forças às quais estejam aptos a suportar. Os diferentes tipos de desadaptações das infraestruturas das próteses sobre implantes são fatores que podem contribuir para o aumento das tensões na região peri-implantar. Este estudo teve como objetivo avaliar a influência das desadaptações angulares unilaterais na distribuição de tensões na região periimplantar de pilares tipo UCLA, no momento da pré-carga e carga axial. Infraestruturas de CoCr, confeccionadas utilizando-se pilares tipo UCLA, foram divididas em quatro grupos: Grupo A (adaptado), Grupo B, Grupo C e Grupo D (50, 100 e 200 μm de desadaptação unilateral angular por vestibular, respectivamente). Cada grupo foi representado por quatro infraestruturas (n=4). Quatro implantes (4.1mm/15mm) foram posicionados em uma matriz metálica, onde posteriormente foi vazado o poliuretano (PU), com função de simular o tecido ósseo. Quatro extensômetros (strain gauges) foram posicionados na região vestibular, distal, lingual e mesial de cada implante, para aferir a quantidade de deformação; cada grupo foi posicionado em seu respectivo implante. Foram realizados dois testes: o teste de pré-carga com um torque de 32Ncm e o teste de carga com uma força axial estática de 300N. Cada infraestrutura foi sujeita aos dois testes, por cinco vezes. Para análise estatística dos dados, foram utilizados ANOVA (dois critérios) e o teste de Tukey (p<0,05). Os resultados mostraram que os grupos A e B tiveram menos deformação da região peri-implantar em ambos os testes, quando comparados aos grupos C e D. A estatística também mostrou que o Grupo A apresentou melhor distribuição de tensões em sua região, peri-implantar quando comparado aos outros três grupos (p<0,05). Como conclusões, este estudo mostrou que as desadaptações influem...

Nowadays implants are used in several kinds of oral rehabilitation treatments. For the osseointegration maintenance it is important that crow/implant/bone are subjected to forces which are able to withstand. Different kinds of misfit on the crown frameworks are factors that could lead to an increase of strain around the implanted bone. This study aimed to evaluate the influence of the unilateral angular misfit in frameworks made of UCLA on the peri-implant strain distribution, subjected to preload and axial load. Frameworks made of chrome-cobalt were fabricated on UCLA abutments and divided in 4 groups: Group A (no misfit), Group B, Group C, Group D (50, 100, and 200 of unilateral angular misfit by buccal side, respectively). Each group was represented for 4 frameworks (n=4). Four implants (4.1mm/15mm) were positioned in a metallic matrix which was subsequently poured the polyurethane (PU) to simulate the bone. Four strain gauges were positioned on the buccal, distal, lingual and mesial sides of each implant to assess the amount of strain, each group was connected on its respectively implant. It was performed 2 tests: the preload test with a 32Ncm torque and the load test by applying an axial force of 300N. Each framework was subjected to the both test five times. To the statistics analysis ANOVA (2 ways) and Turkeys test were performed. The results showed that the Groups A and B presented less deformation when compared to Groups C and D. The statistics also showed that the Group A presented better distribution of strain on its peri-implant bone when compared to the other three groups (p<0,05). In conclusion this study showed that misfit had influence on the strain distribution on the peri-implant bone and that strain increased on the Groups C and D which presented higher levels of misfit.

Deformation of implant abutments after framework connection using strain gauges.

When a cylinder is connected to an abutment it is expected that abutment and cylinder will be subjected to compression forces throughout their periphery because of the clamping force exerted by the screw. The deformation resultant of this compression should be measurable and uniform along the periphery of the abutment. Considering that multiple retainers connected to each other can affect the fit of a framework, as well as the use of different alloys, it is expected that the abutments will present different levels of deformation as a result of framework connection. The aim of this study was to evaluate the deformation of implant abutments after frameworks, cast either in cobalt-chromium (CoCr) or silver-palladium (AgPd) alloys, were connected. Samples (n  =  5) simulating a typical mandibular cantilevered implant-supported prosthesis framework were fabricated in cobalt-chromium and silver-palladium alloys and screwed onto standard abutments positioned on a master-cast containing 5 implant replicas. Two linear strain gauges were fixed on the mesial and distal aspects of each abutment to capture deformation as the retention screws were tightened. A combination of compressive and tensile forces was observed on the abutments for both CoCr and AgPd frameworks. There was no evidence of significant differences in median abutment deformation levels for 9 of the 10 abutment aspects. Visually well-fit frameworks do not necessarily transmit load uniformly to abutments. The use of CoCr alloy for implant-supported prostheses frameworks may be as clinically acceptable as AgPd alloy.

Análise da rugosidade superficial de diferentes marcas comerciais de resina acrílica para coroas provisórias / Surface roughness analysis of acrylic resin for provisional crowns under different commercial brands

As coroas provisórias apresentam algumas características que podem comprometer a estética e facilitar aderência de microorganismos e formação de placa. Estudos prévios demonstraram que a forma de processamento influi na rugosidade e porosidade de uma marca comercial de resina acrílica comumente utilizada para a confecção de provisórias. Como diferentes marcas comerciais apresentam diferenças de qualidade, o presente estudo teve como objetivo principal avaliar a rugosidade superficial de quatro marcas comerciais de resina acrílica utilizadas na confecção de coroas provisórias (Dencor, Vipi, Duralay e Alike) de acordo com quatro técnicas de manipulação, diretas e indiretas. Os processamentos avaliados foram: GRUPO I – autopolimerização sob pressão em matriz de silicona; GRUPO II - autopolimerização térmica em mufla; GRUPO III – autopolimerização utilizando a técnica do pincel; GRUPO IV – autopolimerização pela mistura em pote dappen. Para cada tipo de processamento foram confeccionados 12 corpos de prova de cada material, totalizando 48 corpos de prova para cada grupo e 192 espécimes ao total. Logo após a confecção dos espécimes foi realizado o teste de rugosidade de superfície (Ra) através de um rugosímetro/perfilômetro. Posteriormente, a superfície dos mesmos foi uniformizada e polida com a utilização de politriz, realizando-se novamente os mesmos testes de rugosidade. Antes do acabamento e polimento de superfície, os resultados encontrados apontaram a maior rugosidade para resina Vipi (4,074 ± 0,541) e técnica da mistura em dappen –grupo IV (3,538 ± 0,509), enquanto que a menor rugosidade foi encontrada para resina Alike (2,671 ± 0,512) e técnica da prensagem em mufla – grupo II (2,733 ± 0,470).

Após acabamento e polimento, a maior rugosidade foi encontrada para resina Vipi (0,207 ± 0,032) e técnica da pressão – grupo I (0,172 ± 0,037), enquanto que a menor rugosidade para resina Alike (0,113 ± 0,036) e técnica da prensagem em mufla – grupo II (0,138 ± 0,027). Com os resultados obtidos, foi possível concluir que a melhor combinação para confecção de coroas provisórias em resina acrílica foi a técnica da prensagem em mufla associada à resina Alike

Provisional crowns have some features that may compromise aesthetics and favor adherence of microorganisms and dental plaque formation. Previous studies have shown that processing may influence roughness and porosity of acrylic resins commonly used to make provisional crowns. Because the several commercial resins available present differences in their quality the aim of this study was to evaluate the surface roughness of four commercial brands of acrylic resins (Dencor, Vipi, Duralay and Alike) according to four manipulation techniques (two direct and two indirect): GROUP I – autopolimerization under pressure in a silicone matrix; GROUP II – autopolymerization in flask; GROUP III - autopolimerization using the bead brush technique; GROUP IV - autopolimerization after mixing in dappen dish. For each type of processing 12 specimens were made of each material, being 48 specimens for each group and 192 specimens in total. After specimens preparation, surface roughness tests (Ra) were performed using a rugosimeter / profilometer (roughness and contour measurement equipment). After, all surfaces were polished for standardization and same roughness tests were performed again. Before finishing and polishing, the results pointed out that Vipi resin presented the highest roughness (4.074 ± 0.541).

Mixing the resin in dappen dish – group IV (3.538 ± 0.509) also presented the highest roughness values regarding the technique. The lowest roughness values were found with Alike resin (2.671 ± 0.512) and flask technique – group II (2.733 ± 0.470). After finishing and polishing techniques, the highest roughness was found with Vipi resin (0.207 ± 0.032) and the autopolymetization under pressure in silicone matrix technique - group I (0.172 ± 0.037). The lowest roughness values were found with Alike resin (0.113 ± 0.036) and flask technique – group II (0.138 ± 0.027). With these results, it was possible to conclude that the best combination for making provisional crowns was the flask technique associated with Alike resin

[The impact on life quality due to oral conditions in people fifty years or above]. / O impacto das condições bucais na qualidade de vida de pessoas com cinquenta ou mais anos de vida.

The objective of this work was to evaluate the influence of socio-demographic variables and oral health conditions in the quality of life of non-institutionalized people aged 50 or above, living in Bauru, São Paulo State. Clinical oral examinations were conducted on a sample of 224 people including dental caries, periodontal disease and usage or need of dental prosthesis according to WHO suggestions for community dental health surveys. They were also asked to answer a questionnaire comprised of 49 questions about the impact of their oral status on the activities of daily living (OHIP). Descriptive statistics and multiple regression analysis were computed with individual scores of each domain as dependent variables. The results were: 60% were retired people, 42% exercise no social activity and 65.5% earned less than three minimum wages. Dentate people had a mean of 15.3 missing teeth, 117 people (53% of the sample) had full dentures. It could be concluded that regression analysis showed no socio-demographic variable but age having a significant impact on quality of life; as people get older oral disorders seems to produce lower impact on quality of life. As it concerns to oral clinical data only periodontal disease showed impact on quality of life.

O impacto das condições bucais na qualidade de vida de pessoas com cinquenta ou mais anos de vida / The impact on life quality due to oral conditions in people fifty years or above

Avaliou-se a influência de variáveis sociodemográficas e as condições bucais na qualidade de vida de 224 indivíduos, com 50 anos ou mais de Bauru (SP). Os dados foram coletados de acordo com o Oral Health Surveys-Basic Methods: índices de cárie, periodontal comunitário, perda de inserção periodontal e uso/necessidade de próteses odontológicas. A percepção do indivíduo sobre suas condições bucais, foi medida pelo Oral Health Impact Profile, com sete domínios: limitação funcional, dor, desconforto psicológico, incapacidades física, psicológica e social e desvantagem. 60 por cento dos indivíduos eram aposentados; 42 por cento sem atividade social; 65,5 por cento com renda mensal de um a três salários mínimos; 53 por cento usavam prótese total superior e, destes, 33 por cento ambas; 1,94 dentes cariados e 5,4 restaurados; OHIP-os impactos sociais foram menos intensos que os físicos/ psicológicos; a idade foi significante em todos os domí­nios; apenas a condição periodontal foi importante para a qualidade de vida. As variáveis sociodemográficas e as condições bucais tiveram pequena variação no OHIP; os impactos sociais foram menos intensos que os físicos/psicológicos na qualidade de vida; a maioria dos entrevistados acusou pelo menos um impacto da saúde bucal na qualidade de vida; os escores do OHIP diminuíram nos grupos de maior idade.

The objective of this work was to evaluate the influence of socio-demographic variables and oral health conditions in the quality of life of non-institutionalized people aged 50 or above, living in Bauru, São Paulo State. Clinical oral examinations were conducted on a sample of 224 people including dental caries, periodontal disease and usage or need of dental prosthesis according to WHO suggestions for community dental health surveys. They were also asked to answer a questionnaire comprised of 49 questions about the impact of their oral status on the activities of daily living (OHIP). Descriptive statistics and multiple regression analysis were computed with individual scores of each domain as dependent variables. The results were: 60 percent were retired people, 42 percent exercise no social activity and 65.5 percent earned less than three minimum wages. Dentate people had a mean of 15.3 missing teeth, 117 people (53 percent of the sample) had full dentures. It could be concluded that regression analysis showed no socio-demographic variable but age having a significant impact on quality of life; as people get older oral disorders seems to produce lower impact on quality of life. As it concerns to oral clinical data only periodontal disease showed impact on quality of life.